1，本司出售的塑胶均可随货提供物性数据、SGS报告 、RoHS(环保)报告、MSDS(出厂证明)报告以及UL黄卡。FDA, LFGB报告,均可开17%增值税
PC/ABS C1200HF PC/ABS C1200HF耐高温PC/ABS C1200HF原料
供应PC/ABS基础创新 C1200HF 耐高温 抗冲击
供应PC/ABS基础创新 C2100
供应PC/ABS基础创新 C6200 阻燃，UV稳定
供应PC/ABS基础创新 C6600
供应PC/ABS基础创新 LG9000 低光泽度,紫外稳定
供应PC/ABS基础创新 MC1300 抗冲击性能，电镀应用
供应PC/ABS基础创新 MC8200 低粘度,高抗冲击性,高延性
供应PC/ABS基础创新 MC8800 耐高温，高抗冲性| SABIC Innovative Plastics CYCOLOY C1200HF PC+ABS (Americas) | |||
|---|---|---|---|
|
|||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow  |
19 g/10 min @Load 5.00 kg, Temperature 260 °C |
19 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D 1238 |
| 24 g/10 min @Load 5.00 kg, Temperature 265 °C |
24 g/10 min @Load 11.0 lb, Temperature 509 °F |
cm^3/10 min Melt Volume Rate; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 114 % | 114 % | 50 mm/min; ISO 527 |
| 150 % | 150 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 4.8 % | 4.8 % | 50 mm/min; ISO 527 |
| 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D 638 |
| 2.36 GPa | 342 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 86.0 MPa | 12500 psi | ISO 178 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.25 GPa | 326 ksi | ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched |
4.80 J/cm @Temperature -30.0 °C |
8.99 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 5.87 J/cm @Temperature 23.0 °C |
11.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) |
34.0 kJ/m² @Temperature -30.0 °C |
16.2 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A |
| 49.0 kJ/m² @Temperature 23.0 °C |
23.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Impact Test |
54.0 J @Temperature -30.0 °C |
39.8 ft-lb @Temperature -22.0 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2; UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | PLC 3; UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | PLC 1; UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ISO 306 |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.19 mm |
HB @Thickness 0.0469 in |
UL 94 |